規格介紹:防熱保暖手套
MAPA 332
產品說明 /
高效的隔溫性能和耐多種化學品腐蝕性能。
產品特色 /
1. 雙針織棉帶來優異的隔溫性能。
2. 壓紋的紋理對滑溜的物體有良好的抓握力。
3. 手套材質厚度的增加使得多用途的耐化學腐蝕性增強了(酸類、脂肪族溶劑)。
4. 無矽樹脂,防止金屬板和玻璃在噴漆前存在痕跡和瑕疵。
5. 材質:氯丁橡膠。
6. 長度:36cm。
6. 耐熱:-30°C ~ 150°C 之作業環境。
抗化性能表 /
Chemical Product | CAS # | Breakthrough time | Permeation | Standard | Degradation | Rating |
1,1,1-Trichloroethane 99% | 71-55-6 | 20 | 1 | ASTM F739 | 1 | - |
1,1,2-Trichloroethane 97% | 79-00-5 | 7 | 0 | ASTM F739 | 2 | - |
1,2 - dichloroethane 99% | 107-06-2 | 6 | 0 | ASTM F739 | NT | NA |
2-Bromo-ethyl acetate 97% | 927-68-4 | 52 | 2 | ASTM F739 | 2 | = |
2-Hydroxyethyl Methacrylate 97% | 868-77-9 | 480 | 6 | ASTM F739 | NT | NA |
2-Propanol (Isopropanol) 99% | 67-63-0 | 450 | 5 | ASTM F739 | 4 | ++ |
2,4-Di-tertiary Butylphenol 99% | 96-76-4 | 29 | 1 | ASTM F739 | NT | NA |
2,6-Dimethyl-4-Heptanone (Diisobutyl Ketone) 80% | 108-83-8 | 56 | 2 | ASTM F739 | 3 | + |
Acetaldehyde 99% | 75-07-0 | 5 | 0 | ASTM F739 | NT | NA |
Acetic acid 10% | 64-19-7 | NT | NT | 4 | NA | |
Acetic acid 50% | 64-19-7 | NT | NT | 4 | NA | |
Acetic acid 99% | 64-19-7 | 210 | 4 | ASTM F739 | 4 | ++ |
Acetic acid 99% | 64-19-7 | 399 | 5 | EN 16523-1:2015 | 4 | ++ |
Acetone 99% | 67-64-1 | 8 | 0 | ASTM F739 | 3 | = |
Acetone 99% | 67-64-1 | 10 | 0 | EN 374-3:2003 | 3 | = |
Acetonitrile 99% | 75-05-8 | 62 | 3 | EN 16523-1:2015 | 4 | ++ |
Acrylate 2-Hydroxyethyl 96% | 818-61-1 | 480 | 6 | ASTM F739 | NT | NA |
Acrylic acid 99% | 79-10-7 | 268 | 5 | EN 16523-1:2015 | 4 | ++ |
Acrylonitrile 99% | 107-13-1 | 19 | 1 | ASTM F739 | NT | NA |
Ammonium hydroxide solution 29% | 1336-21-6 | 265 | 5 | ASTM F739 | 4 | ++ |
Amyl Acetate 99% | 628-63-7 | 25 | 1 | ASTM F739 | 2 | = |
Amyl Alcohol 99% | 71-41-0 | 480 | 6 | ASTM F739 | 4 | ++ |
Aniline 99% | 62-53-3 | 142 | 4 | ASTM F739 | 4 | ++ |
Benzene 99% | 71-43-2 | 3 | 0 | ASTM F739 | NT | NA |
Benzotrichloride 100% | 98-07-7 | 63 | 3 | ASTM F739 | NT | NA |
Benzoyl Chloride 100% | 98-88-4 | 28 | 1 | ASTM F739 | NT | NA |
Benzyl Chloride 99% | 100-44-7 | 17 | 1 | ASTM F739 | 2 | = |
Butyl Acetate 99% | 123-86-4 | 17 | 1 | ASTM F739 | 1 | - |
Butyl Acetate 99% | 123-86-4 | 13 | 1 | EN 374-3:2003 | 1 | - |
Butyl Acrylate 99% | 141-32-2 | 15 | 1 | ASTM F739 | 1 | - |
Calcium Hydroxide 0,18% | 1305-62-0 | 480 | 6 | ASTM F739 | 4 | ++ |
Carbon disulfide 99% | 75-15-0 | 1 | 0 | ASTM F739 | 3 | = |
Carbon Tetrachloride 99% | 56-23-5 | 24 | 1 | ASTM F739 | 3 | = |
Chlorine 100% | 7782-50-5 | 480 | 6 | ASTM F739 | NT | NA |
Chlorine 99% | 7782-50-5 | 44 | 2 | ASTM F739 | NT | NA |
Chloroform 99% | 67-66-3 | 2 | 0 | ASTM F739 | NT | NA |
Chromic Acid 50% | 7738-94-5 | 348 | 5 | ASTM F739 | 4 | ++ |
Cumene 98% | 98-82-8 | 22 | 1 | ASTM F739 | 1 | - |
Cyclohexane 99% | 110-82-7 | 35 | 2 | ASTM F739 | 3 | + |
Cyclohexane 99% | 110-82-7 | 39 | 2 | EN 374-3:2003 | 3 | + |
Cyclohexanol 99% | 108-93-0 | 480 | 6 | ASTM F739 | 4 | ++ |
Cyclooctadiene 99% | 111-78-4 | 23 | 1 | ASTM F739 | NT | NA |
Dibutyl Phthalate 99% | 84-74-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Dichloromethane (Methylene Chloride) 99% | 75-09-2 | 4 | 0 | ASTM F739 | 3 | = |
Diethylamine 98% | 109-89-7 | 4 | 0 | ASTM F739 | NT | NA |
Dimethyl Sulfide 99% | 75-18-3 | 2 | 0 | ASTM F739 | 1 | - |
Dimethylformamide 99% | 68-12-2 | 30 | 1 | ASTM F739 | 3 | = |
Dimethylsulfoxide 99% | 67-68-5 | 456 | 5 | ASTM F739 | 4 | ++ |
Diphenyl Phospite NA | 4712-55-4 | 480 | 6 | ASTM F739 | NT | NA |
Ethanol 95% | 64-17-5 | 363 | 5 | ASTM F739 | 4 | ++ |
Ether (Diethyl Ether) 99% | 60-29-7 | 4 | 0 | ASTM F739 | 3 | = |
Ethyl acetate 99% | 141-78-6 | 8 | 0 | ASTM F739 | NT | NA |
Ethyl acrylate 99% | 140-88-5 | 18 | 1 | ASTM F739 | 1 | - |
Ethyl acrylate 99% | 140-88-5 | 15 | 1 | EN 374-3:2003 | 1 | - |
Ethyl benzene 99% | 100-41-4 | 1 | 0 | ASTM F739 | NT | NA |
Ethyl Chloroformate 97% | 541-41-3 | 4 | 0 | ASTM F739 | 2 | - |
Ethylene glycol 99% | 107-21-1 | 480 | 6 | ASTM F739 | 4 | ++ |
Formaldehyde 37% | 50-00-0 | 480 | 6 | ASTM F739 | 4 | ++ |
Formaldehyde 37% | 50-00-0 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Formic Acid 96% | 64-18-6 | NT | NT | 4 | NA | |
Fuel oils mixture | 68476-34-6 | 480 | 6 | ASTM F739 | NT | NA |
Glutaraldehyde 50% | 111-30-8 | NT | NT | 4 | NA | |
Hexachlorocyclopentadiene 100% | 77-47-4 | 30 | 1 | ASTM F739 | NT | NA |
Hydrazine 35% | 302-01-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Hydrazine 70% | 302-01-2 | NT | NT | 4 | NA | |
Hydrochloric acid 10% | 7647-01-0 | 480 | 6 | ASTM F739 | 4 | ++ |
Hydrochloric acid 35% | 7647-01-0 | NT | NT | 4 | NA | |
Hydrochloric acid 37% | 7647-01-0 | 480 | 6 | ASTM F739 | 4 | ++ |
Hydrofluoric Acid 10% | 7664-39-3 | 480 | 6 | ASTM F739 | 4 | ++ |
Hydrofluoric Acid 40% | 7664-39-3 | 480 | 6 | EN 16523-1:2015 | NT | NA |
Hydrofluoric Acid 49% | 7664-39-3 | 480 | 6 | ASTM F739 | 4 | ++ |
Hydrogen fluoride Anhydrous 99% Gas | 7664-39-3 | 35 | 2 | ASTM F739 | NT | NA |
Hydrogen peroxide 30% | 7722-84-1 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Hypophosphorous Acid 50% | 6303-21-5 | 480 | 6 | ASTM F739 | NT | NA |
Isobutyl alcohol 99% | 78-83-1 | 480 | 6 | ASTM F739 | 4 | ++ |
m,o,p-Chlorotoluene mixture | 25168-05-2 | 15 | 1 | ASTM F739 | NT | NA |
Maleic Acid 9,1% | 110-16-7 | 480 | 6 | ASTM F739 | 4 | ++ |
meta-Xylene 99% | 108-38-3 | NT | NT | 2 | NA | |
Methanol 85% | 67-56-1 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Methanol 99% | 67-56-1 | 262 | 5 | EN 16523-1:2015 | 4 | ++ |
Methyl Ethyl Ketone (2-Butanone) 99% | 78-93-3 | 9 | 0 | ASTM F739 | 1 | - |
Methyl methacrylate 95% | 80-62-6 | 15 | 1 | EN 374-3:2003 | 1 | - |
Methylamine 40% | 74-89-5 | 391 | 5 | ASTM F739 | 4 | ++ |
Methylisobutylketone 99% | 108-10-1 | 19 | 1 | ASTM F739 | 2 | = |
Mineral Spirits 100% | 64475-85-0 | 127 | 4 | ASTM F739 | NT | NA |
n-Butanol 99% | 71-36-3 | 480 | 6 | ASTM F739 | 4 | ++ |
n-Heptane 99% | 142-82-5 | 50 | 2 | ASTM F739 | 4 | + |
n-Heptane 99% | 142-82-5 | 82 | 3 | EN 16523-1:2015 | 4 | ++ |
n-hexane 95% | 110-54-3 | 36 | 2 | ASTM F739 | 4 | + |
N-methyl-2-Pyrrolidone 99% | 872-50-4 | 71 | 3 | EN 16523-1:2015 | NT | NA |
N-N dimethyl acetamide 99% | 127-19-5 | 45 | 2 | ASTM F739 | 2 | = |
n-Propanol 99% | 71-23-8 | 480 | 6 | ASTM F739 | 4 | ++ |
N,N-Diisopropylethylamine 99% | 7087-68-5 | 301 | 5 | ASTM F739 | 4 | ++ |
Naphtha (Stoddart Solvent) mixture | 8052-41-3 | 241 | 5 | ASTM F739 | 3 | ++ |
Naphtha Heavy mixture | 68551-17-7 | NT | NT | 4 | NA | |
Naphtha VM&P mixture | 8032-32-4 | 23 | 1 | ASTM F739 | 4 | + |
Nitric acid 10% | 7697-37-2 | NT | NT | 4 | NA | |
Nitric acid 20% | 7697-37-2 | NT | NT | 4 | NA | |
Nitric acid 40% | 7697-37-2 | NT | NT | 4 | NA | |
Nitric acid 50% | 7697-37-2 | NT | NT | 4 | NA | |
Nitric acid 65% | 7697-37-2 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Nitric acid 68% | 7697-37-2 | NT | NT | 4 | NA | |
Nitric acid 70% | 7697-37-2 | NT | NT | 4 | NA | |
Nitric acid 90% | 7697-37-2 | 3 | 0 | ASTM F739 | NT | NA |
Nitrobenzene 99% | 98-95-3 | 52 | 2 | ASTM F739 | NT | NA |
Nonylphenol 99% | 25154-52-3 | 480 | 6 | ASTM F739 | NT | NA |
Oleic Acid 90% | 112-80-1 | NT | NT | 3 | NA | |
Oleum (free SO3) 30% | 8014-95-7 | 10 | 0 | ASTM F739 | NT | NA |
Parachlorobenzotrichloride 99% | 5216-25-1 | 70 | 3 | ASTM F739 | NT | NA |
Pentane 99% | 109-66-0 | NT | NT | 4 | NA | |
Phenol 85% | 108-95-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Phosphoric acid 75% | 7664-38-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Phosphoric acid 85% | 7664-38-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Potassium Hydroxide 50% | 1310-58-3 | 480 | 6 | ASTM F739 | 4 | ++ |
Potassium Iodide 59% | 7681-11-0 | 480 | 6 | ASTM F739 | 4 | ++ |
Propylene Oxide 99% | 75-56-9 | 1 | 0 | ASTM F739 | NT | NA |
Pyridine 99% | 110-86-1 | 10 | 0 | ASTM F739 | 1 | - |
Sodium Carbonate 21,6% | 497-19-8 | 480 | 6 | ASTM F739 | 4 | ++ |
Sodium hydroxide 20% | 1310-73-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Sodium hydroxide 20% | 1310-73-2 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Sodium hydroxide 40% | 1310-73-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Sodium hydroxide 40% | 1310-73-2 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Sodium hydroxide 50% | 1310-73-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Sodium hydroxide 50% | 1310-73-2 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Sodium Thiosulfate 41,2% | 7772-98-7 | 480 | 6 | ASTM F739 | 4 | ++ |
Styrene 99% | 100-42-5 | 2 | 0 | ASTM F739 | NT | NA |
Sulfur Dichloride 100% | 10545-99-0 | 30 | 1 | ASTM F739 | NT | NA |
Sulfur Monochloride 100% | 10025-67-9 | 480 | 6 | ASTM F739 | NT | NA |
Sulfuric acid 10% | 7664-93-9 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Sulfuric acid 40% | 7664-93-9 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Sulfuric acid 96% | 7664-93-9 | 88 | 3 | ASTM F739 | 2 | + |
Sulfuric acid 96% | 7664-93-9 | 190 | 4 | EN 374-3:2003 | 2 | + |
t-Butyl Methyl Ether 98% | 1634-04-4 | 6 | 0 | ASTM F739 | NT | NA |
tert-Butyl Hydroperoxide 70% | 75-91-2 | 454 | 5 | ASTM F739 | NT | NA |
Tetrachloroethylene (Perchloroethylene) 99% | 127-18-4 | 7 | 0 | ASTM F739 | 1 | - |
Tetrahydrofurane 99% | 109-99-9 | 3 | 0 | ASTM F739 | 3 | = |
Toluene 99% | 108-88-3 | 6 | 0 | ASTM F739 | 1 | - |
Toluene 99% | 108-88-3 | 5 | 0 | EN 374-3:2003 | 1 | - |
Trichloroethylene 99% | 79-01-6 | 1 | 0 | ASTM F739 | NT | NA |
Triethylamine 99% | 121-44-8 | 35 | 2 | ASTM F739 | 2 | = |
Trifluoroacetic Acid 99% | 76-05-1 | 480 | 6 | ASTM F739 | 4 | ++ |
Unleaded gasoline mixture | 8006-61-9 | 8 | 0 | ASTM F739 | 1 | - |
Vinyl acetate 99% | 108-05-4 | 14 | 1 | ASTM F739 | 2 | = |
Xylene 99% | 1330-20-7 | 17 | 1 | ASTM F739 | 1 | - |