防酸鹼溶劑手套
防酸鹼溶劑手套
規格介紹:防酸鹼溶劑手套
MAPA 450
產品說明 /
為標準的化學防護提供非常靈活的活動自由。
產品特色 /
1. 氯丁橡膠的柔軟性和棉絨襯裡的舒適性使得手部能夠活動自如。
2. 壓紋紋理提供了良好的抓握力。
3. 材質:Neoprene (氯丁橡膠)。
4. 長度:長41cm。
5. 厚度:0.75mm。
抗化性能表 /
Chemical Product | CAS # | Breakthrough time | Permeation | Standard | Degradation | Rating |
1-Octanol 99% | 111-87-5 | 217 | 4 | ASTM F739 | 4 | ++ |
1,1,1-Trichloroethane 99% | 71-55-6 | 18 | 1 | EN 374-3:2003 | 1 | - |
2-Butoxyethanol (Butyl Cellusolve) 99% | 111-76-2 | 100 | 3 | EN 374-3:2003 | 3 | ++ |
2-Nitropropane 99% | 79-46-9 | 26 | 1 | EN 374-3:2003 | 3 | = |
2-Propanol (Isopropanol) 99% | 67-63-0 | 286 | 5 | EN 374-3:2003 | 4 | ++ |
Acetic acid 10% | 64-19-7 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Acetic acid 50% | 64-19-7 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Acetic acid 99% | 64-19-7 | 391 | 5 | EN 16523-1:2015 | 4 | ++ |
Acetone 99% | 67-64-1 | 10 | 0 | ASTM F739 | 4 | = |
Acetone 99% | 67-64-1 | 15 | 1 | EN 374-3:2003 | 4 | + |
Acetonitrile 99% | 75-05-8 | 28 | 1 | ASTM F739 | 4 | + |
Acetonitrile 99% | 75-05-8 | 11 | 1 | EN 374-3:2003 | 4 | + |
Butyl Acetate 99% | 123-86-4 | 22 | 1 | EN 374-3:2003 | 1 | - |
Cyclohexane 99% | 110-82-7 | 38 | 2 | EN 374-3:2003 | 3 | + |
Dichloromethane (Methylene Chloride) 99% | 75-09-2 | 4 | 0 | ASTM F739 | 1 | - |
Dichloromethane (Methylene Chloride) 99% | 75-09-2 | 3 | 0 | EN 374-3:2003 | 1 | - |
Diethylamine 98% | 109-89-7 | 9 | 0 | ASTM F739 | 1 | - |
Diethylamine 98% | 109-89-7 | 7 | 0 | EN 374-3:2003 | 1 | - |
Dimethylformamide 99% | 68-12-2 | 53 | 2 | ASTM F739 | 4 | + |
Dimethylformamide 99% | 68-12-2 | 42 | 2 | EN 374-3:2003 | 4 | + |
Dimethylsulfoxide 99% | 67-68-5 | 360 | 5 | EN 374-3:2003 | 4 | ++ |
Ethanol 95% | 64-17-5 | 372 | 5 | EN 16523-1:2015 | 4 | ++ |
Ethyl acetate 99% | 141-78-6 | 8 | 0 | ASTM F739 | 3 | = |
Ethyl acetate 99% | 141-78-6 | 12 | 1 | EN 374-3:2003 | 3 | = |
Ethylene glycol 99% | 107-21-1 | NT | NT | 4 | NA | |
Formaldehyde 37% | 50-00-0 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Hydrochloric acid 10% | 7647-01-0 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Hydrochloric acid 35% | 7647-01-0 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Hydrofluoric Acid 40% | 7664-39-3 | 480 | 6 | EN 16523-1:2015 | NT | NA |
Hydrofluoric Acid 49% | 7664-39-3 | 480 | 6 | EN 374-3:2003 | NT | NA |
Hydrogen fluoride Anhydrous 99% Gas | 7664-39-3 | 25 | 1 | ASTM F739 | NT | NA |
Hydrogen peroxide 30% | 7722-84-1 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Methanol 99% | 67-56-1 | 70 | 3 | ASTM F739 | 4 | ++ |
Methanol 99% | 67-56-1 | 226 | 4 | EN 16523-1:2015 | 4 | ++ |
Methyl Ethyl Ketone (2-Butanone) 99% | 78-93-3 | 9 | 0 | EN 374-3:2003 | 2 | - |
Methyl methacrylate 95% | 80-62-6 | 9 | 0 | EN 374-3:2003 | 2 | - |
Methylisobutylketone 99% | 108-10-1 | 20 | 1 | EN 374-3:2003 | 2 | = |
n-Heptane 99% | 142-82-5 | 73 | 3 | EN 16523-1:2015 | 3 | ++ |
n-hexane 95% | 110-54-3 | 30 | 1 | ASTM F739 | 4 | + |
N-methyl-2-Pyrrolidone 99% | 872-50-4 | 101 | 3 | EN 16523-1:2015 | 3 | ++ |
N-N dimethyl acetamide 99% | 127-19-5 | 32 | 2 | ASTM F739 | 3 | + |
Naphtha, Hydrotreated Heavy mixture | 64742-48-9 | 113 | 3 | EN 374-3:2003 | 4 | ++ |
Nitric acid 10% | 7697-37-2 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Nitric acid 20% | 7697-37-2 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Nitric acid 40% | 7697-37-2 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Nitric acid 50% | 7697-37-2 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Nitric acid 65% | 7697-37-2 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Nitric acid 68% | 7697-37-2 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Nitrobenzene 99% | 98-95-3 | 41 | 2 | ASTM F739 | 2 | = |
Phosphoric acid 75% | 7664-38-2 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Sodium hydroxide 20% | 1310-73-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Sodium hydroxide 20% | 1310-73-2 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Sodium hydroxide 40% | 1310-73-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Sodium hydroxide 40% | 1310-73-2 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Sodium hydroxide 50% | 1310-73-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Sodium hydroxide 50% | 1310-73-2 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Styrene 99% | 100-42-5 | 12 | 1 | EN 374-3:2003 | 1 | - |
Sulfuric acid 10% | 7664-93-9 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Sulfuric acid 40% | 7664-93-9 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Sulfuric acid 50% | 7664-93-9 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Sulfuric acid 96% | 7664-93-9 | 36 | 2 | ASTM F739 | 4 | + |
Sulfuric acid 96% | 7664-93-9 | 204 | 4 | EN 16523-1:2015 | 4 | ++ |
t-Butyl Methyl Ether 98% | 1634-04-4 | 18 | 1 | EN 374-3:2003 | 2 | = |
Tetrachloroethylene (Perchloroethylene) 99% | 127-18-4 | 16 | 1 | ASTM F739 | 1 | - |
Tetrachloroethylene (Perchloroethylene) 99% | 127-18-4 | 11 | 1 | EN 374-3:2003 | 1 | - |
Tetrahydrofurane 99% | 109-99-9 | 3 | 0 | ASTM F739 | 1 | - |
Tetrahydrofurane 99% | 109-99-9 | 7 | 0 | EN 374-3:2003 | 1 | - |
Toluene 99% | 108-88-3 | 6 | 0 | EN 374-3:2003 | 1 | - |
Trichloroethylene 99% | 79-01-6 | 6 | 0 | EN 374-3:2003 | 1 | - |
Vinyl acetate 99% | 108-05-4 | 7 | 0 | EN 374-3:2003 | 2 | - |
Xylene 99% | 1330-20-7 | 10 | 0 | EN 374-3:2003 | 1 | - |