規格介紹:特用化學手套(潔淨室用手套)
MAPA 517
產品說明 /
獨特的三聚體材質提供全面的舒適性和優化的耐機械和耐化學性。
產品特色 /
1. 對多種化學品具有優異的耐腐蝕性和強有力的防化能力: 由天然乳膠、氯丁橡膠和丁腈混合而成的特殊配方。
2. 低敏感性的。
3. 確保控制低水平污染物的生產過程: 顆粒含量,非揮發性殘留物,萃取物 => 清洗,控制和包裝在ISO 5 空間以內。
4. 無矽樹脂,防止金屬板和玻璃在噴漆前存在痕跡和瑕疵。
5. 寬袖口有助於手套雙層穿戴。
抗化性能表 /
Chemical Product | CAS # | Breakthrough time | Permeation | Standard | Degradation | Rating |
1,1,1-Trichloroethane 99% | 71-55-6 | 7 | 0 | ASTM F739 | NT | NA |
1,1,1,2,2,3,4,5,5,5-Decafluoropentane 97% | 138495-42-8 | 13 | 1 | ASTM F739 | NT | NA |
1,1,2-Trichlorotrifluoroethane (Freon TF or Freon 113) 99% | 76-13-1 | 20 | 1 | ASTM F739 | 1 | - |
1,2 Dichloroethylene 98% | 156-60-5 | 2 | 0 | ASTM F739 | 2 | - |
1,3 Ethoxy propionate (Ethyl 3-ethoxypropionate) 99% | 763-69-9 | 480 | 6 | ASTM F739 | NT | NA |
2-Butoxyethanol (Butyl Cellusolve) 99% | 111-76-2 | 53 | 2 | ASTM F739 | NT | NA |
2-Butoxyethylacetate (Butyl cellosolve acetate) 85% | 112-07-2 | 35 | 2 | ASTM F739 | NT | NA |
2-Ethoxyethanol (Cellosolve) 99% | 110-80-5 | 27 | 1 | ASTM F739 | NT | NA |
2-Ethoxyethyl acetate (Cellosolve Acetate) 99% | 111-15-9 | 14 | 1 | ASTM F739 | 4 | + |
2-Methoxyethanol (Methyl Cellosolve) 99% | 109-86-4 | 40 | 2 | ASTM F739 | NT | NA |
2-Methoxyethanol Acetate (Methyl cellosolve acetate) 98% | 110-49-6 | 27 | 1 | ASTM F739 | NT | NA |
2-Propanol (Isopropanol) 99% | 67-63-0 | 38 | 2 | ASTM F739 | 4 | + |
2-Propanol (Isopropanol) 99% | 67-63-0 | 29 | 1 | EN 374-3:2003 | 4 | + |
4,4 - diamino diphenylsulfone 97% | 80-008-0 | 480 | 6 | ASTM F739 | NT | NA |
4,4'-Methylenedianiline (MDA) 15% and 15% Methanol mixture | 101-77-9 | 19 | 1 | ASTM F739 | NT | NA |
4,4'-Methylenedianiline (MDA) 15% in Toluene mixture | 101-77-9 | 15 | 1 | ASTM F739 | NT | NA |
Acetic acid 10% | 64-19-7 | NT | NT | 4 | NA | |
Acetic acid 50% | 64-19-7 | NT | NT | 4 | NA | |
Acetic acid 99% | 64-19-7 | 32 | 2 | ASTM F739 | 4 | + |
Acetic acid 99% | 64-19-7 | 29 | 1 | EN 374-3:2003 | 4 | + |
Acetone 99% | 67-64-1 | 6 | 0 | ASTM F739 | 4 | = |
Aluminum Etch mixture | NA | 960 | 6 | ASTM F739 | 4 | ++ |
Aluminum Oxide mixture | NA | 55 | 2 | ASTM F739 | NT | NA |
Ammonium Fluoride 40% | 12125-01-8 | 480 | 6 | ASTM F739 | NT | NA |
Ammonium Fluoride 79% | 12125-01-8 | 480 | 6 | ASTM F739 | NT | NA |
Ammonium hydroxide solution 29% | 1336-21-6 | 36 | 2 | ASTM F739 | 4 | + |
Ammonium hydroxide solution 29% | 1336-21-6 | 19 | 1 | EN 374-3:2003 | 4 | + |
Baker PRS-1000 mixture | NA | 20 | 1 | ASTM F739 | NT | NA |
Baker PRS-2000 mixture | NA | 130 | 4 | ASTM F739 | NT | NA |
Baker PRS-3000 mixture | NA | 480 | 6 | ASTM F739 | NT | NA |
Benzene 99% | 71-43-2 | 4 | 0 | ASTM F739 | 1 | - |
Buffered Oxide Etch mixture | NA | 480 | 6 | ASTM F739 | 4 | ++ |
Butyl Acetate 99% | 123-86-4 | 7 | 0 | ASTM F739 | 4 | = |
Butyl Acetate 99% | 123-86-4 | 5 | 0 | EN 374-3:2003 | 4 | = |
Chromic Acid 50% | 7738-94-5 | 60 | 2 | ASTM F739 | NT | NA |
Cyclohexanone 99% | 108-94-1 | 23 | 1 | ASTM F739 | 1 | - |
Cyclopentanone 99% | 120-92-3 | 11 | 1 | ASTM F739 | NT | NA |
Dichloromethane (Methylene Chloride) 99% | 75-09-2 | 4 | 0 | ASTM F739 | NT | NA |
Dichromate cleaning solution mixture | NA | 480 | 6 | ASTM F739 | 4 | ++ |
Diethylamine 98% | 109-89-7 | 4 | 0 | ASTM F739 | NT | NA |
Diglycidal ether of bisphenol 100% | 25068-38-6 | 480 | 6 | ASTM F739 | NT | NA |
Dimethylamine 35% | 124-40-3 | 53 | 2 | ASTM F739 | NT | NA |
Dimethylformamide 99% | 68-12-2 | 8 | 0 | ASTM F739 | NT | NA |
Dimethylsulfoxide 99% | 67-68-5 | 181 | 4 | ASTM F739 | 4 | ++ |
Epichlorohydrin 99% | 106-89-8 | 4 | 0 | ASTM F739 | NT | NA |
Ethanol 95% | 64-17-5 | 21 | 1 | ASTM F739 | NT | NA |
Ethyl lactate 95% | 97-64-3 | 29 | 1 | ASTM F739 | NT | NA |
Ethylene glycol 99% | 107-21-1 | 480 | 6 | ASTM F739 | 4 | ++ |
Formaldehyde 37% | 50-00-0 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Hexamethyldisilazane (HMDS) 98% | 999-97-3 | 18 | 1 | ASTM F739 | 1 | - |
Hydrochloric acid 10% | 7647-01-0 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Hydrochloric acid 35% | 7647-01-0 | NT | NT | 4 | NA | |
Hydrochloric acid 37% | 7647-01-0 | 454 | 5 | ASTM F739 | 4 | ++ |
Hydrofluoric Acid 10% | 7664-39-3 | 480 | 6 | EN 374-3:2003 | 4 | ++ |
Hydrofluoric Acid 40% | 7664-39-3 | 480 | 6 | EN 16523-1:2015 | NT | NA |
Hydrofluoric Acid 49% | 7664-39-3 | 390 | 5 | ASTM F739 | NT | NA |
Hydrofluoric Acid 49% | 7664-39-3 | 480 | 6 | EN 374-3:2003 | NT | NA |
Hydrogen peroxide 30% | 7722-84-1 | 960 | 6 | ASTM F739 | 4 | ++ |
Hydrogen peroxide 30% | 7722-84-1 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Hydrotreated Light Naphthenic Distillate mixture | 64742-53-6 | 161 | 4 | ASTM F739 | 2 | + |
Kerosene mixture | 8008-20-6 | 26 | 1 | ASTM F739 | 1 | - |
KOH Etch mixture | NA | 278 | 5 | ASTM F739 | 4 | ++ |
KTI Pad Etch mixture | NA | 480 | 6 | ASTM F739 | NT | NA |
KTI Silicon Etch mixture | NA | 480 | 6 | ASTM F739 | NT | NA |
Methanesulfonic Acid 99% | 75-75-2 | NT | NT | 4 | NA | |
Methanol 85% | 67-56-1 | 19 | 1 | ASTM F739 | 4 | + |
Methanol 99% | 67-56-1 | NT | NT | 4 | NA | |
Methyl Amyl Ketone 98% | 110-43-0 | 8 | 0 | ASTM F739 | 1 | - |
Methyl Ethyl Ketone (2-Butanone) 99% | 78-93-3 | 4 | 0 | ASTM F739 | 3 | = |
Methyl-3-methoxypropionate 100% | 3852-09-3 | 11 | 1 | ASTM F739 | 3 | = |
n-hexane 95% | 110-54-3 | 3 | 0 | ASTM F739 | 1 | - |
N-methyl-2-Pyrrolidone 99% | 872-50-4 | 50 | 2 | ASTM F739 | 4 | + |
N-methyl-2-Pyrrolidone 99% | 872-50-4 | 33 | 2 | EN 374-3:2003 | 4 | + |
N-N dimethyl acetamide 99% | 127-19-5 | 47 | 2 | ASTM F739 | NT | NA |
Naphtha VM&P mixture | 8032-32-4 | 2 | 0 | ASTM F739 | 1 | - |
Nitric acid 10% | 7697-37-2 | 840 | 6 | ASTM F739 | 4 | ++ |
Nitric acid 20% | 7697-37-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Nitric acid 40% | 7697-37-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Nitric acid 50% | 7697-37-2 | NT | NT | 4 | NA | |
Nitric acid 68% | 7697-37-2 | 299 | 5 | EN 374-3:2003 | 4 | ++ |
Nitric acid 70% | 7697-37-2 | 307 | 5 | ASTM F739 | 4 | ++ |
Nitric acid 90% | 7697-37-2 | 7 | 0 | ASTM F739 | NT | NA |
Nitride Etch mixture | NA | NT | NT | 4 | NA | |
Nitrohydrochloric acid (Aqua Regia) mixture | 8007-56-5 | 480 | 6 | ASTM F739 | NT | NA |
Phenol 85% | 108-95-2 | 102 | 3 | ASTM F739 | 4 | ++ |
Phosphoric acid 75% | 7664-38-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Phosphoric acid 85% | 7664-38-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Phosphorus Oxychloride 99% | 10025-87-3 | 15 | 1 | ASTM F739 | NT | NA |
Piranha Etch mixture | NA | 243 | 5 | ASTM F739 | 1 | - |
Polyethylene glycol octylphenyl ether 100% | 9002-93-1 | 480 | 6 | ASTM F739 | NT | NA |
Potassium Hydroxide 50% | 1310-58-3 | 480 | 6 | ASTM F739 | 4 | ++ |
Potassium Hydroxide Etch mixture | NA | 24 | 1 | ASTM F739 | NT | NA |
Propylene Glycol 99% | 57-55-6 | 480 | 6 | ASTM F739 | 4 | ++ |
Propylene Glycol Methyl Ethyl Acetate (PGMEA) 99% | 108-65-6 | 47 | 2 | ASTM F739 | 3 | + |
Propylene Glycol Monomethyl Ether 99% | 107-98-2 | 26 | 1 | ASTM F739 | 4 | + |
Silicon Tetrachloride 100% | 10026-04-7 | 15 | 1 | ASTM F739 | NT | NA |
Slope Etch mixture | NA | 260 | 5 | ASTM F739 | 4 | ++ |
Sodium hydroxide 20% | 1310-73-2 | 780 | 6 | ASTM F739 | 4 | ++ |
Sodium hydroxide 20% | 1310-73-2 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Sodium hydroxide 40% | 1310-73-2 | 780 | 6 | ASTM F739 | 4 | ++ |
Sodium hydroxide 40% | 1310-73-2 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Sodium hydroxide 50% | 1310-73-2 | 780 | 6 | ASTM F739 | 4 | ++ |
Sodium hydroxide 50% | 1310-73-2 | 480 | 6 | EN 16523-1:2015 | 4 | ++ |
Sulfuric acid 10% | 7664-93-9 | 900 | 6 | ASTM F739 | 4 | ++ |
Sulfuric acid 96% | 7664-93-9 | 102 | 3 | ASTM F739 | 3 | ++ |
Sulfuric acid 96% | 7664-93-9 | 41 | 2 | EN 374-3:2003 | 3 | + |
Tetrachloroethylene (Perchloroethylene) 99% | 127-18-4 | 4 | 0 | ASTM F739 | 1 | - |
Tetrachloroethylene (Perchloroethylene) 99% | 127-18-4 | 3 | 0 | EN 374-3:2003 | 1 | - |
Tetraethyl Orthosilicate 100% | 78-10-4 | 25 | 1 | ASTM F739 | 1 | - |
Tetramethyl Ammonium Hydroxide 25% | 75-59-2 | 480 | 6 | ASTM F739 | 4 | ++ |
Thionylchloride 99% | 7719-09-7 | 15 | 1 | ASTM F739 | NT | NA |
Toluene 49% Methyl Isobutyl Ketone 34.5% Methyl Ethyl Ketone 16.5% mixture | NA | 1 | 0 | EN 374-3:2003 | NT | NA |
Toluene Diisocyanate (TDI) 80% | 584-84-9 | 27 | 1 | ASTM F739 | NT | NA |
Trichloroethylene 99% | 79-01-6 | NT | NT | 1 | NA | |
Trimethylphosphite 97% | 121-45-9 | 10 | 0 | ASTM F739 | NT | NA |
Unleaded gasoline mixture | 8006-61-9 | 4 | 0 | ASTM F739 | 1 | - |
Xylene 99% | 1330-20-7 | 4 | 0 | ASTM F739 | 1 | - |
Xylene 99% | 1330-20-7 | 3 | 0 | EN 374-3:2003 | 1 | - |